Effective Hydrogen Diffusion Coefficient and Microstructural Behaviors Measured by Electrochemical Hydrogen Permeation for CoCrFeMnNi High-Entropy Alloy

  • Save

... pages left unread,continue reading

Document pages: 18 pages

Abstract: Herein, the first observation of the effective hydrogen diffusion coefficient of CoCrFeMnNi high-entropy alloy (HEA) was performed using electrochemical hydrogen permeation; further, it was compared with those of Fe-17Cr-10Ni and Fe-18Cr-8Ni stainless steels (SS). HEA and Fe-17Cr-10Ni SS showed similar effective hydrogen diffusion coefficient of 1.75×10-11m2 s and 1.91×10-11 m2 s, respectively. Fe-18Cr-8Ni SS showed the smallest that of 0.58×10-11 m2 s in the study. Hydrogen diffusion through the grain boundary was dominant in face-centered cubic metals. Hydrogen permeation resulted in no change in the microstructure of HEA and Fe-17Cr-10Ni SS; however, it caused a martensitic transformation in Fe-18Cr-8Ni SS.

Please select stars to rate!


0 comments Sign in to leave a comment.

    Data loading, please wait...